Titanium Clad Copper Wire Diameter 2 - 6.35mm For Cathodic Protection

Our ISO 9001:2015 certificate

The process of the titanium clad copper wire is explosion and hot rolled, details please check follows:

The explosion method firstly puts the copper rod into the titanium tube, uniformly distributes the explosive material outside the titanium tube, and uses the detonator to detonate the explosive, so that the copper rod and the titanium tube form a composite under the action of the explosive force. Since the cross-sectional size of the titanium-copper composite rod is generally small, the production yield by the explosion method is low, resulting in high cost, and no one in the industrial production currently adopts this method.

Explosion + rolling method is to use a larger size of titanium tube and copper rod, the blank is made by the explosion method, and then the finished composite rod is produced by the method of hole rolling. Compared with the direct explosion method, this method has the advantages of improving efficiency and reducing cost. The composite rods produced by the composite strength and other indicators are also good. However, since the rolling processing amount should not be too large, that is, the elongation coefficient is not large, it is not suitable for mass production. and for a rectangular composite rod, the corners are not easily filled. If the amount of deformation of the pass is not well controlled, there may be a crimp or ear. Due to the use of the finished hot rolling method, the composite rod has poor bending resistance and has an impact on the use.